Effect of Jordanian Steel Blast Furnace Slag on Asphalt Concrete Hot Mixes
Abstract
Significant quantities of slag are generated as waste materials or by-product from steel industries. They usually contain considerable quantities of metals. In this study, steel slag obtained from a steel factory in Jordan was used in Asphalt Concrete Hot Mixes (ACHM). Marshall specimens were prepared with 100% lime stone dense graded aggregates at 4.5, 5, 5.5 and 6% bitumen contents by weight of aggregate to serve as control specimens. Another set of Marshall specimens with 100% Steel Slag Aggregates (SSA) and another set with a combination of limestone and (SSA) were prepared using the same grading and bitumen contents. Test results showed a reduction in the Optimum Bitumen Content (OBC) and an increase in density and stability values for specimens prepared with 100% (SSA). A decrease in the flow, Percentage of air voids (Pav), and Voids in Mineral Aggregates (VMA) values - but in compliance with the recommended values by the Asphalt Institute- was observed in specimens prepared with 100% (SSA).
To list your conference here. Please contact the administrator of this platform.
ISSN: 1993-0461 ISSN: 2225-157X,
Edited and Published by Jordan University of Science and Technology, P.O.Box 3030, Irbid 22110, Jordan
Mailing address: Prof. Fouad Gharaybeh, Ph.D.
Editor-in-Chief Civil Engineering Department Jordan University of Science and Technology Irbid 22110, Jordan Tel. No. + 962 2 7201000 ext. 22104 Fax No. + 962 2 7201073
Submission & Subscriptions E-mail:jjce@just.edu.jo