The effect of temperature on preparation of nano material via dopping ZP in mesoporous activated carbon
Abstract
A nano material was obtained by dopping ZP in mesoporous nanocarbon which prepared by physical activation carbon via thermal effect .A series of ZP materials dopped in activated carbon obtained from DP by physical activation. The dopped ZP-C materials were heat-treated at various temperatures, 100–800 0C. TGA & DTG thermal analysis showed that incorporation of the doping agent within the carbon DP layered materials which enhanced the heat-resistivity of the nanohybrid materials in the thermal decomposition pathway. Porous carbon materials can be obtained from the heat-treatment of the nanohybrids at 700 and 900 0C. Calcination of the dopped material was achieved at 9000C under nitrogen atmosphere which produces mesoporous and high pore volume carbon materials. According to the kinetics of Freeman–Carroll and Coats–Redfern the calculated order of reaction of ZP in DP is 2. The calculated activation energy of both matrices are 402 and 350 kJ mol–1.
Key Words: Activated carbon; solid waste DP; physical activation; ZP; and nanotechnology
![Download the IISTE publication guideline!](https://www.iiste.org/sub/iiste_footer_journal.jpg)
To list your conference here. Please contact the administrator of this platform.
Paper submission email: CMR@iiste.org
ISSN (Paper)2224-3224 ISSN (Online)2225-0956
Please add our address "contact@iiste.org" into your email contact list.
This journal follows ISO 9001 management standard and licensed under a Creative Commons Attribution 3.0 License.
Copyright © www.iiste.org