Dielectric Properties and AC conductivity of (Epoxy / Ion exchange) blend

Abstract

The dielectric behavior of blend materials epoxy resin- Polyvinyl benzyl dimethyl ethanol ammonium chloride (PBDEAC) (Ion exchange) was analysed as a function of Ion exchange  weight content; temperature and frequency. Blends were prepared by mixing the components and pouring them into suitable moulds. The dielectric parameters have been measured using parallel plate capacitor method in the frequency range from 120 Hz to 2 MHz and in the temperature range from 30 ^?C to 110^?C. Variations of real (??) and imaginary (?") parts of dielectric constants and loss tangent of material with frequency and temperature have been studied. The experimental results showed that (??) and (?") increased with the addition of Ion exchange filler content. The value of (??) decreased with increasing frequency, which indicates that the major contribution to the polarization comes from orientation polarization. Dielectric loss peaks were also observed in the composite materials at high temperature. The value of (??) increased with increasing temperature, and is due to greater freedom of movement of the dipole molecular chains within the polymer at high temperature. Ac. conductivity and impedance of the composites behaviours as function of frequency and temperature have also been investigated.

Keywords: Dielectric properties, epoxy, Ion exchange, ac. conductivity_.