Effect of Addition of PET in the Thermal Properties of Polymer-Mortar Composite Materials

Abstract

The polymer-mortar composites are often used as low-cost promising materials for preventing or repairing various reinforced concrete structures. The Thermal behavior of the ¶building materials ¶is relevant to any use of concrete or composite, especially in relation to structures where it is desirable to have low thermal conductivity, dimensional stability, high specific heat and little or no decrease of stiffness upon heating. Although much work has been done on the effect of admixture and the mechanical properties of concrete or composite, relatively little work has been done on the thermal conductivity. So, Thermal conductivity (l), thermal resistance (R) and the surface coefficients of transmission (U) of polymer-mortar composites made up of mixtures of polyethylene terephthalate PET waste were measured. To determine the effect of the PET on the thermal conductivity of PET-mortar composites, PET was added as replacement for cement by decreasing the cement weights in the ratios of 2.5%, 5% and 7.5% by weight. The highest thermal conductivity of 1.45 W/mK was observed with the samples containing only plain cement. It decreased with the increase of PET as replacement for cement. The lowest value of thermal conductivity and the surface coefficient of transmission were obtained with the samples prepared with PET waste polymer at 7.5 % replacement of cement. The composites were also observed by DTA, MOP led to the positive identification of the products’. In this way, the results obtained highlight the beneficial effect of waste PET as thermal insulation in comparison with other insulation materials. In addition, the obtained PET-mortar composites would appear to be low-cost materials which would contribute to resolving some of the solid waste problems in addition to conserving energy.